I-AGS ibonakalisa elubala ukusuka kwi-0.50 ukuya kwi-13.2 µm.Nangona i-coefficient yayo ye-optical nonlinear iyeyona iphantsi phakathi kweekristale ze-infrared ezikhankanyiweyo, i-wavelength ecacileyo yokukhanya kwe-edging kwi-550 nm isetyenziswe kwii-OPO ezimpontshwa yi-Nd: YAG laser;kwimifuniselo emininzi yokudityaniswa okuphindaphindiweyo ngediode, iTi:Sapphire, Nd:YAG kunye neIR yelaser yedayi egubungela uluhlu lwe-3-12 µm;kwiinkqubo ezithe ngqo ze-infrared countermeasure, kunye ne-SHG ye-CO2 laser.Iipleyiti zekristale eziNcinci ze-AgGaS2 (AGS) zithandwa kakhulu kwi-ultrashort pulse ephakathi kuluhlu lwe-IR ngokwahlukana kwesizukulwana esisebenzisa i-NIR wavelength pulses.
Iipropati ezisisiseko | |
Iiparamitha zeLattice | a = 5.757, c = 10.311 Å |
I-coefficient engekho mgca kwi-10.6 um | d36 = 12.5 pm/V |
Umda womonakalo we-Optical kwi-10.6 um, i-150 ns | 10 - 20 MW / cm2 |
ihambelana ne-c-axis | 12.5 x 10-6 x °C-1 |
perpendicular to c-axis | -13.2 x 10-6 x °C-1 |
Ulwakhiwo lweCrystal | I-Tetragonal |
Iiparamitha zeSeli | a=5.756 Å, c=10.301 Å |
Indawo yokunyibilika | 997 °C |
Ukuxinana | 4.702 g/cm3 |
Mohs Ubunzima | 3-3.5 |
I-Absorption Coefficient | 0.6 cm-1 @ 10.6 µm |
Relative Dielectric Constant @ 25 MHz | ε11s=10ε11t=14 |
I-Coefficient yoKwandiswa kweThermal | ||C: -13.2 x 10-6 /oC⊥C: +12.5 x 10-6 /oC |
I-Thermal Conductivity | 1.5 W/M/°C |
IiParameters zobuGcisa | |
Ukugqwetheka kwamaza | ngaphantsi kwe λ/6 @ 633 nm |
Ukunyamezela komlinganiselo | (W +/-0.1 mm) x (H +/-0.1 mm) x (L +0.2 mm/-0.1 mm) |
Umngxuma ocacileyo | > 90% indawo esembindini |
Ukucaba | λ/6 @ 633 nm ye T>=1.0mm |
Umgangatho womphezulu | Scratch / dig 20/10 nge-MIL-O-13830A |
Ukufana | ngcono kune-1 arc min |
Perpendicularity | 5 arc imizuzu |
Ukunyamezela i-angle | Δθ < +/-0.25o, Δφ < +/-0.25o |
Umzekelo | Imveliso | Ubungakanani | Ukuqhelaniswa | Umphezulu | Ntaba | Ubungakanani |
DE0742-1 | AGS | 5*5*0.4mm | θ=39°φ=45° | AR/AR@1.1-2.6μm+2.6-12μm | Ayinyuswanga | 6 |
DE0053 | AGS | 5*5*0.5mm | θ=41.3°φ=0° | AR/AR@1.1-2.6μm+2.6-12μm | Ayinyuswanga | 1 |
DE0741 | AGS | 5*5*1mm | θ=39°φ=45° | Omabini amacala akhazimlisiwe | Ayinyuswanga | 1 |
DE0743 | AGS | 6*6*2mm | θ=54.9°φ=45° | Omabini amacala akhazimlisiwe | Ayinyuswanga | 1 |
DE0891-1 | AGS | 6*6*2mm | θ=50°φ=0° | Omabini amacala akhazimlisiwe | Ayinyuswanga | 3 |
DE0149 | AGS | 8*8*0.38mm | θ=41.6°φ=45° | AR/AR@1.1-2.6μm+2.6-12μm | Ayinyuswanga | 1 |
DE0367 | AGS | 8*8*0.4mm | θ=39°φ=45° | AR/AR@1.1-2.6μm+2.6-12μm | φ25.4mm | 1 |
DE0367-0 | AGS | 8*8*0.4mm | θ=39°φ=45° | AR/AR@1.1-2.6μm+2.6-12μm | Ayinyuswanga | 8 |
DE0367-1 | AGS | 8*8*0.4mm | θ=37°φ=45° | AR/AR@1.1-2.6μm+2.6-12μm | Ayinyuswanga | 8 |
DE0367-2 | AGS | 8*8*0.4mm | θ=37°φ=45° | AR/AR@1.1-2.6μm+2.6-12μm | φ25.4mm | 1 |
DE0367-3 | AGS | 8*8*0.4mm | θ=39°φ=45° | AR/AR@1.1-2.6μm+2.6-12μm | φ25.4mm | 1 |
DE0119 | AGS | 8*8*1mm | θ=39°φ=45° | AR/AR@1.1-2.6μm+2.6-12μm | φ25.4mm | 3 |
DE0119-0 | AGS | 8*8*1mm | θ=39°φ=45° | AR/AR@1.1-2.6μm+2.6-12μm | φ15.4mm | 3 |
DE0119-1 | AGS | 8*8*1mm | θ=37°φ=45° | AR/AR@1.1-2.6μm+2.6-12μm | Ayinyuswanga | 7 |
DE0119-3 | AGS | 8*8*1mm | θ=39°φ=45° | AR/AR@1.1-2.6μm+2.6-12μm | Ayinyuswanga | 5 |
DE0671 | AGS | 8*8*1mm | θ=39°φ=45° | Omabini amacala akhazimlisiwe | Ayinyuswanga | 1 |
DE0957 | AGS | φ3*0.4mm | θ=39°φ=45° | AR/AR@1.1-2.6μm+2.6-12μm | φ25.4mm | 1 |